Oxy-Acetylene Welding

oxy-acetylene welding operating principle





Oxyacetylene welding uses the concept of generating heat from the combustion of oxygen and fuel gas. Gas supply stored in high-pressure cylinders flows through the flexible hoses (an oxygen hose and a fuel gas hose) by adjusting the gas regulators. The gases are combined in the mixing chamber of the hand-held oxy-fuel torch and exit through the orifice in the tip. Welding tip orifice size is an important factor and thus, it should be chosen in accordance with the application.

As heat is applied to the base metal, it reaches a melting point (around 3200°C), wherein fusion welding occurs. Other welding techniques that use electricity can reach higher temperatures (above 5000°C), making oxyacetylene welding most suitable for thin metals. Using filler rods is optional and depends on the scope of the project.

Since gas welding operates with combustible materials, it is vital to practice proper safety measures.

Types of Flames

The type of welding flame plays an important role in determining the resulting weld joint and its properties. The flame profile is manipulated by adjusting the fuel gas and oxygen flow rate.

Higher amounts of oxygen lead to a hotter flame, which might cause the metal to warp. A colder flame occurs when the amount of fuel gas is higher than oxygen, which might cause poor weld quality.

Neutral Flame

Equal amounts of welding gases by volume result in a neutral flame. The complete combustion of the fuel gas and compressed oxygen means that the properties of the weld metals aren’t affected while producing minimal smoke at the same time.

This welding flame has two zones, a white inner zone of about 3100°C and a blue outer zone with a temperature of about 1275°C. Neutral flame is preferred when welding metals such as cast iron, mild steel and stainless steel.

Carburising Flame

Carburising aka reducing flame is achieved by supplying higher amounts of fuel gas compared to pure oxygen. The flame produced is smoky and has a quiet flame that chemically forms metal carbide.

Three zones are produced in this flame: a white inner zone (2900°C), a red intermediate zone (2500°C), and a blue outer zone (1275°C). Carburising flame is preferred for welding nickel, steel alloys and non-ferrous metals.

Oxidising Flame

Oxidising flames are produced when the supplied gas from the oxygen cylinder is higher than the fuel gas – the excess oxygen results in higher flame temperatures exiting the welding torch than neutral flame.

This type of flame produces two zones, a white inner zone at around 3500°C and a blue outer zone at 1275°C. Oxidising flame is used for welding metals such as brass, copper, bronze and zinc.



Welding Techniques

Leftward

The torch travels from the right to the joint’s left side with a tip forming a 60-70 degree work angle to the workpiece. The filler material is angled at 30 to 40 degrees to the plate. Three movements create uniform fusion through its flame: circular, rotational, or side-to-side.

Leftward welding is mainly used to weld unbevelled plates up to 5mm, cast iron, and non-ferrous metals.

Rightward

Opposite to leftward welding, the rightward technique starts at the left side of the joint and travels towards the right end. An angle of 40-50 degrees is established between the torch tip and the workpiece, while the filler rod makes a 30-40 degree angle to the work material.

Rightward welding is generally faster than leftward welding, with less distortion, and filler metal consumed. It creates denser and stronger welds, which are perfect for protection against contamination.

All-Positional Rightward

This technique is a modification to rightward welding used mainly for steel plate welding, also some pipework and butt welds (5-8mm thick) wherein complete view and movement are required.

Vertical

The joint is created with an oscillating rod and torch travelling from the bottom toward the top. The rod makes a 30-degree angle, while the torch makes a 25 to 90-degree angle with the workpiece, depending on its thickness.

A single operator may use this technique for steel plates up to 5 mm thick, while two operators working in harmony are required for thicker metals.

Materials

  • Aluminium

  • Brass

  • Bronze

  • Carbon steels

  • Cast iron

  • Copper

  • Magnesium

  • Mild steel

  • Nickel

  • Stainless steel

  • Steel alloys

  • Zinc

Advantages of Gas Welding

  1. The process is suitable for a variety of ferrous and non-ferrous metals.

  2. Gas welding doesn’t require electricity.

  3. It is a simple and straightforward welding technique.

  4. Gas welding equipment is cheap and portable compared to other welding processes.

Disadvantages of Gas Welding

  1. Gas welding offers less penetration and heat than arc welding techniques, such as TIG and MIG welding.

  2. The process requires post-weld finishing to improve its aesthetic look.

  3. Oxyacetylene welding is prone to weld defects since it doesn’t have weld pool shielding.

  4. Gas welding has a slower rate of heating and cooling compared to modern methods.

  5. It isn’t suitable for welding high-strength steel since it can alter its mechanical properties.

Wrapping It Up

Oxy-fuel welding is one of the pioneers of the industrial revolution, offering versatility in its wide range of applications. Today, it is not much used in industries as it has been before, as newer and more innovative welding techniques have replaced it. Still, gas welding remains a reliable choice for some applications and is preferred by some hobbyists and professionals.

Comments

Post a Comment

Popular posts from this blog

mig welding

Image
  Torch Position and Laying Welds It pays to practice a bit laying beads on the sheet metal you plan to use to develop some technique before trying any project welding upside down on a rusty car. If you plan to mess around with cars a good thickness for the first practice sessions would be 1.5mm or 2mm. 1.5 or 2mm is thick enough to stop blowing holes becoming a big issue, and is a handy thickness to use for experimentation with power settings. Preparing the metal Metal needs to be completely clean of rust or paint in the area where you want to weld. Any rust or paint will act as an electrical insulator which isn't good when you are are using an electric welder. An area needs to be cleaned for the earth clamp too. Light use of a flap disc on an angle grinder will quickly remove surface rust and paint without thinning the metal. For more inaccessible areas an air grinder or dremmel can be effective. Holding the torch MIG can be used one handed but nobody does that because it can be ...
Read more

TIG Filler Rods types

Image
TIG Filler Rods Explained A TIG filler rod is a special metal alloy that withstands high heat and does not lose its characteristics after melting and solidifying. The primary role of TIG rods is to add the additional metal to the weld joint and help fuse the two pieces, creating high-quality welds with a desirable strength. A TIG welding rod is similar to a MIG wire, and they share the composition. However, there are various types of TIG filler metals, and they differ on the: Composition (Type) Diameter Length Choosing the suitable TIG filler metal will depend on the type and thickness of the metal you are welding. As a rule of thumb, you want the rod to have the same composition as the base metal and one size smaller than the metal thickness, but let's explore this further. TIG Filler Rod Types For Various Metals To help welders make an informed choice when choosing the right tig filler metal, AWS (American Welding Society) created a classification. The system for identifying the ...
Read more